Go to Editorial ManagerThe aim of this work is to optimize EPD variables (voltage, time, and focus) using alternating current through the Taguchi Design of Experiment (DOE). Coating Nano hydroxyapatite (Nano-HA) on a Ti6Al4V substrate depends on thickness and roughness, then characterization of a coating layer to determine the optimum state. Hydroxyapatite (HAp) powder was deposited on a Ti-6Al-4V alloy substrate by electro-deposition with ethanol as a solvent under AC current, to improve the alloy surface quality based on coating thickness and maximum coating mass meeting the requirements of a biological orthopedics application. Ethanol was used as a solvent to precipitate ketazone and HAp on the base alloy. Taguchi's approach was used in order to determine the optimal conditions for EPD and subsequently to apply various criteria for depositing the biochemical coating. The surface and cross-section composition of the paint is described by characterization. Numerous tests and inspections; Zeta, XRD and SEM stability test, water contact angle and optical microscopes were used to describe the surface morphology of the HAp layer. The value of the optimum conditions for deposition of the HAp layer which is a simultaneous thickness and maximum coating mass, was predicted at a sedimentation voltage of 40 V, 2 min sedimentation time and 1 g / L for the concentration of the suspended solution at room temperature. The validity of the model resulting from the response surface methodology was assessed by comparing the expected results with the experimental results. In addition, close agreement was observed between the experimental results and the expected results. For the solution at room temperature, the results obtained with the highest value of the coating thickness of 41at the surface roughness of 0.94 and the contact angle of the alloy before coating is 67.489º reduced to. 38.132º after plating, which indicates an increase in the harmony of the metal implant and biocompatibility.
In this study the friction stir lap welding was carried out by a new technique (diffusion bonding phenomenon) between (AA1100 and low carbon steel C10 sheets of 3mm and 1mm thickness respectively. These alloys have difference ranges in melting temperature and other physical properties. Different parameters were used: tool rotation speeds (630, 1250) rpm, travel speeds (80, 32) mm/min. and pin length (2.8,3) mm using cylindrical threaded pin. Many tests and inspections were performed such as tensile shear test and X-Ray diffraction tests. Microhardness and microstructure observations were conducted by using optical and SEM. The above tests were used to evaluate the weld quality and joint efficiency under different welding parameters. Best result for FSLW by diffusion phenomenon appear in (low carbon steelC10 / AA1100-H112) joint at 1250rpm in 32 mm/min. with 2.8mm pin length and the maximum tensile shear strength was (3.9)KN.It was found that the highest micro hardness was (138HV) at the interface between the low carbon steel and AA1100.