Go to Editorial ManagerThe aim of this work is to investigate the effect of soil corrosion on the critical buckling load of circular columns made of 2014-T4 aluminum alloy. In this work, 24 specimens were used and buried in the soil for 120 days. The samples divided into two groups (12 columns with corrosion before shot penning (SP) and ultrasonic impact treatment (UIT), and 12 columns with corrosion after combined surface treatments (SP+UIT)). The experimental1results revealed1that the corrosion negatively1affects the mechanical properties1of the material, and the1reduction percentage (R%) for1ultimate tensile strength (UTS) and1yield strength (YS) was (1.95% and 4.57%) respectively. After combined surface treatments (SP+UIT) for the corroded columns, the ultimate1tensile strength (UTS) and yield1strength (YS) were improved with (2.42%, and 2.87%) respectively. Perry-Robertson, Rankine, and ANSYS were used to estimate the critical buckling load (Pcr) and compare it with the experimental results. Rankine and Perry's formulas have been achieved a good agreement with the experimental without and with (1.5) factor of safety respectively. While ANSYS gave satisfactory prediction with a safety factor of (2.2, and 2.7) and (1.9, and 2.7) for long and intermediate columns before and after (SP+UIP) respectively.
This research deals with the extent to which corrosion affects the behavior of buckling for 6061-T4 aluminum alloy under increasing compressive dynamic loads. Two types of columns, long, and intermediate were used.1% of the length column is the allowable lateral deflection. This is called the critical buckling of the columns. For the purpose of calculating the critical deflection, a digital dial gauge was used and set at a distance of 0.7 of column length from the fixed end condition for the column. The experimental analysis revealed that the corrosion time negatively affects the mechanical properties of materials such as the corroded specimens of 60 days (The least time to observe the corrosion of aluminum in the soil) which have approximately 2.7 % reduction in ultimate strength compared with the non-corroded specimen. Increasing the corrosion time reduces the critical load such as the maximum reduction will be 4.24% in critical buckling load for 60 days’ corrosion time. The results obtained were experimentally compared with the theoretical formulas of the Perry-Robertson and Euler-Johnson formula with the results of the ANSYS. It was found that the Perry-Robertson formula has a good agreement with the experimental results with a safety factor of 1.2, while the Euler-Johnson formula agreed with the experimental results taking a safety factor of 1.5. The ANSYS results showed a good agreement between the measured and calculated values by taking 1.1 factor of safety.