The submission system is temporarily under maintenance. Please send your manuscripts to
Go to Editorial ManagerWelding residual stress has influences on fatigue, fracture, and corrosion. It is therefore important to explore the welding factors effect on the residual stresses. In this work, four welding factors (current, arc voltage, welding travel speed and included angle) were used to weld low carbon steel (ASTM A516 Grade 60).The experiments included welding of (60) pieces with dimensions of (300 x 150) mm and 10 mm thickness that were conducted based on the design matrix founded by using design of experiment (DOE) software (DESIGN EXPERT 10) with response surface methodology (RSM) technique. The X-Ray diffraction (XRD) method was used to measure the residual stress, which was then modeled and optimized in terms of the welding factors using (RSM) technique. The data showed that the welding travel speed and arc voltage have a significant influence on the residual stress. It was found that the optimum solution for minimum residual stress was at 450 Amp welding current, 34 volt arc voltage, 38 cpm welding speed, and 60? included angle. Where, the optimum value of residual stress was (-88.4 MPa). Finally, the predicted and experimental results of residual stress were in agreement with a maximum error of 1.8%.
Orthoses and prostheses were Chosen and laminated based on their high Yield, ultimate stresses, bending stresses, and fatigue limit. Response Surface Methodology (RSM) was utilized to find the best values for two parameters reinforcement perlon fiber and percent of Titanium Nanoparticle coupled with the matrix resin during optimization. The response surface methodology combined the expertise of mathematicians and statisticians to construct and analyze experimental models. Using this method, we identified 13 different lamination samples comprising a wide range of perlon number and Ti nano Wt% in their Perlon layer composition. All lamination materials defined by RSM methods and produced by a vacuum system were subjected to a battery of tests, with fatigue tests performed on the ideal laminating material in contrast to laminations created in the first study (Tensile test, Bending test, and Fatigue tests according to the ASTM D638 and D790 respectively). In comparison to the other 12 laminations tested using Design Expert version 10.0.2, the lamination with ten perlon layers and 0.75 percent Ti nano proved to be the strongest overall in terms of Yield, ultimate, and bending loads. This study used composite materials and titanium nanoparticles to characterize and fabricate ankle foot orthoses. Strength in bending should amount to about 70 MPa, around 85 MPa in tensile tension. Two empirical quadratic equations for the models of peak bending strength and maximum tensile stress with 95% confidence were created using the response surface approach and analysis of variance within the design of experiments software.
Biodiesel produced from vegetable oils is a good alternative clean diesel. The present study was conducted because there are some variations or contradictions in literature on the use of CaO heterogeneous catalyst. In this study, biodiesel was produced from sunflower vegetable oil and methanol in presence of commercial calcium oxide catalyst in batch mechanical stirrer reactor. The effect of three operating conditions, methanol mole ratio (4-12), reaction time (0.5-2.5 h) and catalyst amount (2-10 %), on the yield of biodiesel was studied at constant reaction temperature of 60 oC. Response surface methodology (RSM) was used with central composite design (CCD) of experiments. Polynomial correlation was found for the dependent variable of the process (yield of biodiesel), satisfactorily predicted at 95% confidence level. The optimum yield biodiesel was about 98% and at operating condition of methanol ratio 10, reaction time 2 h and catalyst amount 8 %. The reaction time was found to be the most effective operating condition. Kinetics study of the process showed that first order reaction with triglyceride concentration and zero order with methanol concentration gave best fit with the experimental data, triglyceride with a reaction rate constant k= 1.53 h-1.
This work describes seam welding process using dissimilar ferrous metals by pulsed Nd:YAG. The main objective of this work is to achieve the best welding conditions. This imposes careful selection for the welding parameters and inevitably the well design of experiment (DOE). Sheets of ASTM A240/316L stainless steel to ASTM A570/Gr30 carbon steel all of 0.5 mm in thickness were lap welded. Different pulse energies or the related peak power, pulse duration, pulse repetition rate, and welding speeds were used. Moreover, different welding speeds were controlled by the employed manipulator. The laser beam spot diameter and the standoff distance were fixed. Experimental results are supported by the computational 2D and 3D models. In this article response surface methodology (RSM) was applied to design the experiment and obtain the best parameters through a set of mathematical models that define the weld characteristics. The results show that the best joint in term of joint strength is obtained at 31.9 J pulse energy (related to 5.5 kW peak power and 5.8 ms pulse duration), power density of 1.43×106 W/cm2, 1.5 Hz pulse repetition rate, and 0.5 mm/s welding speed.
This work investigated the removal of the reactive green (R.G) dye from wastewater using the photo-Fenton process. Batch experiments were carried out to research the role of the Impacts of operating parameters. The dosage of H2O2; dosage Fe+2; pH; temperature, and irradiation time were examined. Maximum decolorization efficiencies green dye were achieved at the [H2O2]=100 ppm; [Fe2+]=20 ppm; pH 3; temperature=56 °C and irradiation time=90 min. This research focuses on modeling, kinetics and thermodynamics of the removal of pollutant (reactive green dye) of water. The results showed that the decolorization kinetic of R.G followed pseudo-first-order reaction kinetic. Also the thermodynamic parameters ?G?, ?H? and ?S? were determined using the Van't Hoff equation for the oxidation processes. The changes in Gibbs free energy showed the oxidation process under normal conditions is non-spontaneous.