The submission system is temporarily under maintenance. Please send your manuscripts to
Go to Editorial ManagerMoisture-induced damage in asphalt pavements, is defined by adhesive failure at the binder-aggregate interface and decreased mechanical integrity, severely reduce pavement durability. The research examines the mechanical properties and moisture sensitivity of hot mix asphalt (HMA) enhanced with styrene-butadiene-styrene (SBS) polymer and including reclaimed asphalt pavement (RAP). Laboratory assessments, including indirect tensile strength (ITS) and tensile strength ratio (TSR) tests, were performed on conventional HMA, SBS-modified HMA (4% SBS), and SBS-modified HMA contained 20% RAP. The results indicated that SBS modification significantly improved mechanical and moisture resistance properties, where unconditioned ITS specimens increased by 37.1% and TSR value enhanced by 13.5%. The incorporation of RAP decreased ITS value by about 21 % relative to pure SBS-modified HMA; nevertheless, the SBS+RAP combination still show higher ITS and TSR values than conventional HMA.
This paper focused on evaluating the effect of aggregate gradation and polymer modification on indirect tensile strength (ITS) and the static stiffness for hot asphalt mixtures. In particular, data from ITS tests have been processed to obtain stiffness measurements through the application of Hondros theory. The results showed that fine mixtures had a better tensile strength by 26.3% than the coarse mixtures. The effect of compaction also was examined, the results showed that samples compacted with the Superpave gyratory compactor (SGC) had an enhancement in ITS by 36.58 and 23.1% in comparison with Marshall and roller compactor respectively. Polymer modifiers were used to estimate their effect on tensile strength, adding 4, 6, and 8% of Styrene-Butadiene-Styrene (SBS), which can rise the ITS by 3.2,6.14 and 13.3% of the non-modified asphalt mixture. Furthermore, using 4, 6, and 8 percent of SBS could increase static stiffness by 53.9, 209.6, and 302.4% respectively for roller compacted fine mixes and 58, 220, and 379.3% for SGC compacted mixes. Furthermore, SBS raised the stiffness modulus by 52.3, 188, and 295% for Marshall compacted mixes. Using hybrid modifier can improve the stiffness of the asphalt mixture. However, The results indicate that using 1, 2 and 3% polyvinyl chloride (PVC) can magnify the stiffness of mixtures by 41.2, 199.8% and 262.6 for roller compacted mixtures and 133.4, 212.1 and 354% for SGC compacted mixtures, whereas there is a stringent increasing by 133.4, 189.2 and 354% for Marshall compacted mixes. Otherwise, polymer-modification can decrease the fracturing index for coarse and fine mixtures.
Open graded asphalt mixture is becoming more widespread where it is applied for various purposes, e.g. drainage of rainwater effectivity, traffic safety (high skid resistance), and controlling pollution noise. However, it has many other disadvantages, of which low stability, high stripping, and moisture sensitivity. The research aims to study the effect of styrene butadiene styrene SBS addition on the volumetric and mechanical properties of open graded mixture. In this research one type of aggregate with gradation (12.5 mm NMAS), asphalt of penetration grade (40/50), and cement as filler were used. Optimum asphalt content was selected based on the criteria of air voids content, asphalt drain down, permeability, and abrasion resistance (for aged and un-aged) samples. Other properties of open-graded mixtures, such as indirect tensile strength (ITS), moisture susceptibility, Marshall stability and flow were evaluated. The results show that addition of polymer (SBS) leads to an enhancement in the properties of the modified mixtures. There is an improvement in Marshall parameters. Also, a slight decreasing is noticed for permeability and air voids. For Cantabro abrasion loss (aging and un-aging condition), the abrasion resistance is increased, the drain down of asphalt is decreased from original mixture by addition of SBS. Finally, the moisture sensitivity is improved indicating that modified mixes becomes more resistant to water damage.
Utilization of additives can be an effective way to improve the durability and performance of HMA, making them more resistant to Moisture and deformation. Plus, they can reduce the need for maintenance and repairs, saving you time and money in the long run. In this study, CKD was used in place of limestone as a filler in the asphalt mixture in proportions of 0%, 25%, 50%, 75%, and 100%, and polymer SBS 4%by weight of asphalt. According to the findings, replacement-content CKD had the highest asphalt content. When the CKD is between 25% and 50%, Stability, Flow, and Indirect Tensile Strength are improved, while the density of the asphalt mixture decreases and the amount of air voids increases at higher ratios. While SBS leads to an increase in the hardness of the adhesives. As a consequence, the stability of the SBS-containing mixes resulted in higher values than the control and additive-containing mixtures (CKD), as well as a decrease in the number of air voids. According to the results, CKD should not constitute more than half of the filler weight in the asphalt mixture.
Rutting is considered as the most generated distress in Iraqi roads as a result of the high temperature and excessive traffic load. So, it is essential to utilize polymer modified binder to increase the performance of pavements. The objective of this paper is to assess the effect of aggregate gradation and filler content on the rutting formation of Colored Hot Mix Asphalt CHMA. The HMA was colored by using iron oxide as filler to produce red HMA. Two blends were used: fine and coarse with two different types of filler iron oxide for CHMA and limestone for conventional HMA with two filler content 6% and 10%. Neat (AC 40-50) and modified asphalt (AC 40-50 + 4%SBS) were used. Tests are held on adding 4% Styrene Butadiene Styrene )SBS( by the weight of neat asphalt (AC 40-50) to raise the performance grade by two grades from PG (64-16) to PG (76-16) [1] and [2]. The wheel tracking test is used to assess the rut depth of the CHMA. The test results showed that the using iron oxide with neat asphalt increase the rut depth resistance by 200 and 400 failure load cycles than mixtures using limestone (cycles that mix reach 25 mm rut depth) for fine and coarse mix respectively. Also, the effect of gradation shows that the fine mixture fails at 4000 cycles while the coarse mixture fails at 1800 cycles for 6% limestone mixtures. Increasing the iron oxide content from 6% to 10% leads to increase the failure load cycles by 2200 and 1200 cycles for fine and coarse mixture respectively using modified asphalt. The fine mixture with 10% iron oxide using modified asphalt gives the best performance with 7000 cycles than the coarse mixture with 10% filler content and modified asphalt with 4000 cycles. irrespective the filler and type of binder, the dense mixtures using iron oxide as filler exhibit better resistance to rutting formation than coarse mixtures.